                                           Classification of large-sized aluminum castings Large-scale

                                                   



Aluminum castings of common shapes generally adopt sand casting technology, so that a strong casting process can be followed, and a casting process mode can be established.

     For large-scale and box-type aluminum castings, it is difficult to control the wall thickness. In the process design, the outer mold and the core box should adopt different casting shrinkage rates. In addition, the core core should be increased.

     Large-scale ring-shaped and plate-type aluminum castings are prone to deformation, and anti-deformation lacing should be prevented for the specific structure and shape of the casting. In addition, the riser is not placed in the casting itself as much as possible, and after the pouring is completed, it is completely cooled and then unpacked.

     If the box type casting contains a separator with a thin thickness and a sharp direction, the casting system should meet the requirement of filling the separator as soon as possible.

评论

发表评论

此博客中的热门博文

-
                Ten things that must be paid attention to in precision casting! 1. Unblock all obstacles to the channel and site. 2. Check if the ladle is dry, whether the bottom of the bag, the ear, the bag and the end are safe and reliable, and whether the rotation is flexible. Do not use dry Iron ladle. 3, all tools in contact with molten iron, must be preheated to 500 degrees Celsius before use, otherwise it should not be used. 4, the ladle should not exceed 80% of the volume, the ladle should be smooth and slow, keep the steps to prevent the overflow of molten iron. Cast iron 5, before the crane crane should check the iron of the hook, the chain is reliable, the chain is not allowed to knot, there is a person responsible for tracking the iron in the water There must be no staff on the line. 6. Strictly implement the "six will not fall": (1) The temperature of molten iron is not enough; (2) The molten iron grade is...
阅读全文
-
图片
                    Understand the importance of defects in precision castings     In actual production, it is often necessary to analyze casting defects, the purpose of which is to find out the cause of the defects so that measures can be taken to prevent them. For precision casting designers, understanding product defects and causes can help to properly design the casting structure and combine the actual conditions of the casting production to properly formulate the technical requirements. There are many defects in precision castings , and the defects and causes are very complicated. Sometimes, defects caused by many different reasons appear on the same casting, or the same reason may cause various defects when the production conditions are different. Whether a defective casting with defects is classified as waste must be determined according to the use and requirements of the casting and the location and severi...
阅读全文
-
图片
                                                                   Factors affecting the surface roughness of stainless steel castings Surface roughness is another major quality indicator for stainless steel castings , generally less than 3.2 μm, between 0.8 and 3.2 μm. There are many factors affecting the surface roughness of castings, such as the pressure type, the surface quality of the investment and stainless steel, the casting process, the type of alloy and other factors. (1) Profile and investment surface quality. The surface roughness of the investment mold is the most important part affecting the surface roughness of the casting, and it is related to the surface quality of the molding, the compression molding method and the pressing process parameters. (2) Stainless steel surface quality. Stainless stee...
阅读全文